Terblend® N NM-19XP

Terblend® N NM-19XP is an ABS/PA blend with excellent impact toughness, very good flowability and UV-stabilization.

Key Features

  • High impact strength
  • Easy processing
  • UV-stabilized

Applications

  • Unpainted automotive interior parts
  • Center consoles
  • Air inlets
  • Steering wheel covers
  • Grade Version
  • Properties

    物性

    23℃での無色製品の標準値 試験方法 単位 数値
    流動学的性質
    Melt Volume Rate, 240 °C/10 kg ISO 1133 cm³/10 min 40
    機械的性質
    Tensile Modulus ISO 527 MPa 2000
    Tensile Stress at Yield, 23 °C ISO 527 MPa 43
    Tensile Strain at Yield, 23 °C ISO 527 % 3.5
    Nominal Strain at Break, 23 °C ISO 527 % 30
    Flexural Modulus, 23 °C ISO 178 MPa 1800
    Flexural Strength, 23 °C ISO 178 MPa 62
    Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 65
    Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 15
    Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 65
    Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 15
    Hardness, Ball Indentation ISO 2039-1 MPa 86
    Tensile Modulus after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 1400
    Tensile Stress at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 34
    Tensile Strain at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 5.5
    Nominal Strain at Break after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 35
    熱的性質
    Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 102
    Vicat Softening Temperature, VST/A/50 (10N, 50 °C/h) ISO 306 °C 160
    Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 100
    Heat Deflection Temperature A; (unannealed; 1.8 MPa) ISO 75 °C 65
    Heat Deflection Temperature B; (unannealed; 0.45 MPa) ISO 75 °C 85
    Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 85
    Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 97
    電気的性質
    Relative Permittivity (1 MHz) IEC 62631-2-1 - 2.9
    Dissipation Factor (1 MHz) IEC 62631-2-1 10-4 150
    Volume Resistivity IEC 62631-3-1 Ω*m >1013
    Surface Resistivity IEC 62631-3-1 Ω 1014
    進行中
    Density ISO 1183 kg/m³ 1070
    Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 1.2
    UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB
    Processing
    Melt Temperature Range ISO 294 °C 240 - 270
    Mold Temperature Range ISO 294 °C 60 - 80
    Drying Temperature - °C 80 - 90
    Drying Time - h 4 - 8
    Molding shrinkage, free, longitudinal - % 0.7

    Typical values for uncolored products
    Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
    Please consult our local sales or technical representatives for details.