Products

K-Resin DK11

K-Resin® DK11 is easily processed on injection molding specificially for medical devices. K-Resin® DK11 has good thermal stability and broader processing window. 

Key Features

  • Excellent Clarity
  • Good Toughness
  • High Surface Gloss
  • Good Stiffness
  • Good Heat Sealability
  • High Gas Permeability

Applications

  • Controlled Atmosphere Packaging
  • Cover Films for IC carrier tape
  • Medical Packaging
  • Decorative Films
  • Lidstock and Labeling Film
  • Twist Wrap
  • Grade Version
  • Properties

    Properties of K-Resin DK11

    Property, Test Condition Standard Unit Values
    Rheological Properties
    Melt Flow Rate, 200 °C/5 kg ASTM D 1238 g/10 min 7,5
    Mechanical Properties
    Elongation at Break (MD) ASTM D 882 % 110
    Elongation at Break (TD) ASTM D 882 % 200
    Elemendorf Tear (MD) ASTM D 1922 lbs 0,02
    Elemendorf Tear (TD) ASTM D 1922 lbs 0,0033
    Puncture, Energy at Peak Force ASTM D 3763 in-lb 8
    Tensile Yield Strength (MD) ASTM D 882 psi 5000
    Tensile Yield Strength (TD) ASTM D 882 psi 3100
    Secant Modulus, 1% MD ASTM D 882 psi 205000
    Secant Modulus, 1% TD ASTM D 882 psi 140000
    Dart Drop, 26 in (66 mm) ASTM D1709 g 590
    Flexural Strength, 23 °C ASTM D 790 psi 5400
    Tensile Strain at Break, 23 °C ASTM D 638 % 230
    Tensile Modulus ASTM D 638 psi x 10³ 220
    Nominal Strain at Break, 23 °C - % 170
    Thermal Properties
    Vicat Softening Temperature, B/1 ( 120 °C/h, 10N) ASTM D 1525 °F 185
    Optical Properties
    Gardner Gloss (mold temperature 100°F) ASTM D2457 % 140
    Haze ASTM D 1003 % 1
    Light Transmission at 550 nm ASTM D 1003 % 92
    Other Properties
    Density (ASTM ) ASTM D 792 g/cm³ 1,01
    Oxygen Transmission Rate (23 °C/0% RH) ASTM D 3985 cc/100in²/day 420
    Water Vapor Transmission Rate (WVTR) (23 °C/0% to 85% RH gradient) ASTM F1249-06 g/100in²/day 5,5

    The nominal properties herein are typical of the product but do not reflect normal testing variance and therefore should not be used for specification purposes. Values are rounded.
    Typical blown film properties with 3% SKR17 slip/antiblock, I mil ( 0.025 mm) film (2.5:1 BUR) 35 mil ( 0.90 mm) die gap.
    [Vicat Softening Point] = Injection Molded Specimen.
    [Haze] = Haze was me asured using blown film containing only 1% SKR19 stabilizer, I mil ( 0.025 mm) film (2.5:1 BUR) 35 mil ( 0.90 mm) die gap.

  • Processing

    Processing of K-Resin DK11

  • Safety Data Sheet