Terblend S NM-31
The product line Terblend® S, comprising blends of ASA with PA 6, provides very good mechanical properties, a high melt flow, and an excellent chemical resistance. The ASA component assures a high UV resistance for all kind of interior applications – incl. unpainted surfaces in light colors – but also for exterior parts with medium weatherability requirements. Parts from Terblend® have acoustic dampening properties and show in unpainted, textured surfaces a nice matt appearance. Terblend® S NM-31 provides a very high melt flow and similar mechanical properties as Terblend® N NM-21EF. It is a low emission grade that can be used e.g. as drop-in solution for unpainted, automotive interior applications in light colours.
Key Features
- Chemical resistance
- High flowability
- High surface quality
- Impact strength
- Colour fastness
Applications
- Unpainted automotive interior: loudspeaker grills, air ventings
- Bicycle/ E-bicycle parts
- Gardening tools
- Toys, sports & leisure
Industries
-
Grade Version
-
Properties
특성
섭씨 23도에서 변색되지 않는 제품에 대한 일반적인 값 테스트 방법 단위 값 유동적 특성 Melt Volume Rate, 240 °C/10 kg ISO 1133 cm³/10 min 60 기계적 특성 Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 70 Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 9 Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 65 Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 8 Tensile Modulus ISO 527 MPa 2100 Tensile Stress at Yield, 23 °C ISO 527 MPa 50 Tensile Strain at Yield, 23 °C ISO 527 % 3.3 Tensile Stress at Break, 23 °C ISO 527 MPa 33 Tensile Strain at Break, 23 °C ISO 527 % 50 Nominal Strain at Break, 23 °C ISO 527 % 25 Tensile Modulus after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 1300 Tensile Stress at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 35 Tensile Strain at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 7 Nominal Strain at Break after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % > 50 Flexural Modulus, 23 °C ISO 178 MPa 2000 Flexural Strength, 23 °C ISO 178 MPa 65 Hardness, Ball Indentation ISO 2039-1 MPa 99 열 특성 Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 110 Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 87 Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 97 Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 100 처리 중 Density ISO 1183 kg/m³ 1070 UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB Glow wire test (GWFI), 2.0 mm IEC 60695-2-12 °C 650 Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 1.5 Processing Melt Temperature Range ISO 294 °C 240 - 270 Mold Temperature Range ISO 294 °C 60 - 80 Drying Temperature - °C 80 - 90 Drying Time - h 4 - 8 Linear Mold Shrinkage ISO 294-4 % 0.7 - 0.9 Typical values for uncolored products
Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
Please consult our local sales or technical representatives for details. -