Terblend® N NM-19XP
Terblend® N NM-19XP is an ABS/PA blend with excellent impact toughness, very good flowability and UV-stabilization.
Key Features
- High impact strength
- Easy processing
- UV-stabilized
Applications
- Unpainted automotive interior parts
- Center consoles
- Air inlets
- Steering wheel covers
Industries
-
Grade Version
-
Properties
属性
无色产品在摄氏 23 度时的典型值 测试方法 单位 数值 流变性能 Melt Volume Rate, 240 °C/10 kg ISO 1133 cm³/10 min 40 机械性能 Tensile Modulus ISO 527 MPa 2000 Tensile Stress at Yield, 23 °C ISO 527 MPa 43 Tensile Strain at Yield, 23 °C ISO 527 % 3.5 Nominal Strain at Break, 23 °C ISO 527 % 30 Flexural Modulus, 23 °C ISO 178 MPa 1800 Flexural Strength, 23 °C ISO 178 MPa 62 Charpy Notched Impact Strength, 23° C ISO 179/1eA kJ/m² 65 Charpy Notched Impact Strength, -30 °C ISO 179/1eA kJ/m² 15 Izod Notched Impact Strength, 23 °C ISO 180/A kJ/m² 65 Izod Notched Impact Strength, -30 °C ISO 180/A kJ/m² 15 Hardness, Ball Indentation ISO 2039-1 MPa 86 Tensile Modulus after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 1400 Tensile Stress at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 MPa 34 Tensile Strain at Yield after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 5.5 Nominal Strain at Break after Moisture Absorption, Equilibrium 23 °C/50% RH ISO 527 % 35 热性能 Vicat Softening Temperature VST/B/50 (50N, 50 °C/h) ISO 306 °C 102 Vicat Softening Temperature, VST/A/50 (10N, 50 °C/h) ISO 306 °C 160 Coefficient of Linear Thermal Expansion ISO 11359 10-6/°C 100 Heat Deflection Temperature A; (unannealed; 1.8 MPa) ISO 75 °C 65 Heat Deflection Temperature B; (unannealed; 0.45 MPa) ISO 75 °C 85 Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa) ISO 75 °C 85 Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa) ISO 75 °C 97 电气性能 Relative Permittivity (1 MHz) IEC 62631-2-1 - 2.9 Dissipation Factor (1 MHz) IEC 62631-2-1 10-4 150 Volume Resistivity IEC 62631-3-1 Ω*m >1013 Surface Resistivity IEC 62631-3-1 Ω 1014 Other Properties Density ISO 1183 kg/m³ 1070 Moisture Absorption, Equilibrium 23 °C/50% RH ISO 62 % 1.2 UL94 rating at 1.5 mm thickness IEC 60695-11-10 - HB Processing Melt Temperature Range ISO 294 °C 240 - 270 Mold Temperature Range ISO 294 °C 60 - 80 Drying Temperature - °C 80 - 90 Drying Time - h 4 - 8 Molding shrinkage, free, longitudinal - % 0.7 Typical values for uncolored products
Please note that all processing data stated are only indicative and may vary depending on the individual processing complexities.
Please consult our local sales or technical representatives for details. -